Hastelloy X (UNS N06002): Hoch-Temperatur Oxidation Resistant Alloy für Aerospace
AMS 5536 / ASTM B435 · Published: 2026-06-02 · Updated: July 2026
Hastelloy X (UNS N06002) is a nickel-chromium-iron-molybdenum alloy designed for exceptional oxidation resistance and high-temperature strength up to 1,200°C. It is the most widely used wrought nickel alloy for aerospace gas turbine hot-section...
Hastelloy X (UNS N06002) ist ein nickel-chromium-iron-molybdenum alloy designed für exceptional oxidation widerstand und hoch-temperature strength auf zu 1,200°C. Es ist der meiste widely used wrought nickel alloy für aerospace gas turbine heiß-abschnitt components: combustor cans, transition ducts, afterburner components, und tail cone assemblies. Der alloy's 22% chromium content forms ein protective Cr2O3 scale; 9% molybdenum provides fest-solution strengthening bei elevated temperatures; und 18.5% iron reduces raw material kosten compared zu mehr nickel-rich superalloys wie Inconel 718.
Fabrication: Hastelloy X ist readily formed in der solution-annealed condition (1,177°C, rapid luft cool oder wasser quench). Es ist weldable durch GTAW (TIG), GMAW (MIG), und widerstand welding — matching filler metal (AMS 5798) müssen sein used. Post-weld stress relief bei 1,080°C für 1 hour ist recommended zu minimize distortion. Der alloy cannot sein age-hardened — alle strengthening ist durch fest solution, und hoch-temperature strength derives von der inherent creep widerstand von der FCC (face-centered cubic) nickel matrix rather als precipitate strengthening. Für applications requiring higher strength bei temperature, precipitation-hardened superalloys (Inconel 718, Waspaloy) sind specified für rotating components, while Hastelloy X remains der standard für static heiß-abschnitt sheet metal components.
Quick Facts
| Kategorie | Nickel Alloy |
| Norm | AMS 5536 / ASTM B435 |
| Density | 8220 kg/m³ |
| Yield Strength | 360 MPa (solution annealed) |
| Tensile Strength | 750 MPa |
Global Equivalents & Cross-Reference
| Alternative Standard / Grade | Action |
|---|---|
| UNS N06002 | Compare |
| Haynes HX | Compare |
| EN 2.4665 NiCr22Fe18Mo9 | Compare |
Verwandt Materials
🧮 Material Weight Calculator
Calculate the weight based on this material's density: 8220 kg/m³
Frequently Asked Questions
Wenn sollte I specify Hastelloy X vs Inconel 625 für hoch-temperature service?
Hastelloy X hat superior oxidation widerstand und slightly higher maximum service temperature (1,200°C vs 1,100°C für 625). Inconel 625 hat higher strength bei intermediate temperatures (600-800°C) due zu niobium precipitation hardening. Für sheet metal static components in oxidizing atmospheres über 1,000°C, Hastelloy X ist preferred. Für components requiring yield strength über 400 MPa bei 650°C, Inconel 625 ist preferred.
References & International Standards
- ASTM International. Norm Specifications für Stahl & Metal Alloys. astm.org
- International Organization für Standardization (ISO). Metallic Materials — Cross-Referenz Database. iso.org
- American Iron und Stahl Institute (AISI). Stahl Güte Designations & Equivalents. steel.org
- European Committee für Standardization (CEN). EN Stahl Standards & Numbering System. cencenelec.eu