C93200 Bearing Bronze (SAE 660) — Leaded Tin Bronze für Bearings, Bushings & Wear Plates
ASTM B584 (UNS C93200, SAE 660) · Published: 2026-06-14 · Updated: July 2026
C93200 (SAE 660) is the most commonly specified bearing bronze worldwide. Its 7% tin + 7% lead + 3% zinc + balance copper composition creates a microstructure of hard copper-tin dendrites (the load-bearing phase) embedded in a soft lead-rich...
C93200 (SAE 660) ist der meiste commonly specified bearing bronze worldwide. Sein 7% tin + 7% lead + 3% zinc + balance copper composition creates ein microstructure von hard copper-tin dendrites (der load-bearing phase) embedded in ein soft lead-rich matrix (der lubricating phase). Wenn der bearing runs, der lead phase smears across der surface, providing emergency lubrication wenn der öl film breaks ab. Dies self-lubricating characteristic ist was makes C93200 forgive der kinds von intermittent lubrication failures das würde seize ein steel-ein-steel bearing instantly.
Der 6-8% lead content ist was differentiates C93200 von non-leaded bronzes wie C90500 (tin bronze, nein lead) oder C90700. Der lead provides machinability (C93200 machines bei approximately 70% von kostenlos-cutting brass — excellent für ein bronze) und embeddability (der ability zu absorb hard dirt particles in der bearing surface rather als letting ihnen score der shaft). Für applications in food processing oder potable wasser wo lead ist prohibited, substitute C89835 (bismuth-tin bronze, ASTM B584) — but expect approximately 15-20% shorter bearing life und higher shaft wear.
Key applications: allgemein-purpose sleeve bearings, pumpe impeller wear rings, thrust washers, worm gears, bridge pins, und marine shaft bearings. Nicht recommended für: hoch-geschwindigkeit applications über 500 SFM (surface feet per minute), operating temperatures über 230°C (450°F), oder highly corrosive environments — verwenden C95400 aluminum bronze oder C95500 nickel aluminum bronze für diese conditions.
Quick Facts
| Kategorie | Copper Alloy |
| Norm | ASTM B584 (UNS C93200, SAE 660) |
| Density | 8930 |
| Yield Strength | 125-150 MPa |
| Tensile Strength | 240-275 MPa |
Global Equivalents & Cross-Reference
| Alternative Standard / Grade | Action |
|---|---|
| SAE 660 | Compare |
| JIS LBC3 | Compare |
| CuSn7Zn4Pb7 | Compare |
| ISO CuSn7Zn4Pb7-C | Compare |
Verwandt Materials
🧮 Material Weight Calculator
Calculate the weight based on this material's density: 8930
Frequently Asked Questions
C93200 vs C95400 — welche bearing bronze sollte I spec?
C93200 (SAE 660) für allgemein-purpose, moderate-load bearings mit gut lubrication. C95400 (aluminum bronze) für hoch-load, hoch-wear, oder corrosive environments — es's roughly twice als strong but requires better lubrication und ist harder ein shafts. Der kosten rule von thumb: wenn C93200 bushings sind lasting bei least 5,000 hours, don't über-spec C95400. Wenn sie're failing vor 2,000 hours oder der environment ist corrosive, upgrade.
Können C93200 sein used in food processing ausrüstung?
Nein — C93200 contains 6-8% lead, welche ist prohibited in food contact applications unter FDA und NSF/ANSI 51. Für lead-kostenlos bearing bronze, spec C89835 (bismuth-tin bronze) für sleeve bearings oder C89833 für continuous cast applications. Diese lead-kostenlos alternatives haben approximately 80-85% von der bearing leistung von C93200.
References & International Standards
- ASTM International. Norm Specifications für Stahl & Metal Alloys. astm.org
- International Organization für Standardization (ISO). Metallic Materials — Cross-Referenz Database. iso.org
- American Iron und Stahl Institute (AISI). Stahl Güte Designations & Equivalents. steel.org
- European Committee für Standardization (CEN). EN Stahl Standards & Numbering System. cencenelec.eu