ASTM A532 Class II Typ D: Hoch-Chromium White Iron für Extreme Abrasion
ASTM A532 · Published: 2026-06-03 · Updated: July 2026
ASTM A532 Class II Type D (20% Cr, 2% Mo) high-chromium white iron achieves 600-700 BHN hardness through a microstructure of M₇C₃ chromium carbides in a martensitic matrix. It is specified for slurry pump impellers, mill liners, chute liners, and...
ASTM A532 Class II Typ D (20% Cr, 2% Mo) hoch-chromium white iron achieves 600-700 BHN hardness durch ein microstructure von M₇C₃ chromium carbides in ein martensitic matrix. Es ist specified für slurry pumpe impellers, mill liners, chute liners, und shot blast machine components wo abrasive wear ist der sole design criterion.
Quick Facts
| Kategorie | Cast Iron |
| Norm | ASTM A532 |
| Density | 7.50 g/cm³ |
| Yield Strength | N/A (brittle) |
| Tensile Strength | 350-500 MPa |
Global Equivalents & Cross-Reference
Verwandt Materials
🧮 Material Weight Calculator
Calculate the weight based on this material's density: 7.50 g/cm³
Frequently Asked Questions
Können hoch-chromium white iron sein machined?
Nein — bei 600-700 BHN, white iron ist harder als meiste cutting tools. Teile müssen sein cast zu near-net shape und finished durch grinding nur. Design features requiring machining (keyways, threaded holes) müssen sein accommodated durch cast-in inserts oder durch designing around der limitation. Dies ist der fundamental tradeoff für extreme abrasion widerstand.
References & International Standards
- ASTM International. Norm Specifications für Stahl & Metal Alloys. astm.org
- International Organization für Standardization (ISO). Metallic Materials — Cross-Referenz Database. iso.org
- American Iron und Stahl Institute (AISI). Stahl Güte Designations & Equivalents. steel.org
- European Committee für Standardization (CEN). EN Stahl Standards & Numbering System. cencenelec.eu