Maraging 300 (18Ni-300): Ultra-Hoch-Strength Stahl für Aerospace Tooling
AMS 6514 / ASTM A538 · Published: 2026-06-02 · Updated: July 2026
Maraging 300 achieves >2,000 MPa yield strength through Ni3Mo/Ni3Ti intermetallic precipitation during aging at 480°C for 3 hours. Unique: 2,000+ MPa strength with KIC >80 MPa√m toughness — no other steel matches this combination. For landing...
Maraging 300 achieves >2,000 MPa yield strength durch Ni3Mo/Ni3Ti intermetallic precipitation während aging bei 480°C für 3 hours. Unique: 2,000+ MPa strength mit KIC >80 MPa√m toughness — nein andere steel matches dies combination. Für landing gear, rocket motor casings, extrusion tooling.
Quick Facts
| Kategorie | Legierungsstahl |
| Norm | AMS 6514 / ASTM A538 |
| Density | 8000 kg/m³ |
| Yield Strength | 1,930-2,070 MPa (aged) |
| Tensile Strength | 2,000-2,100 MPa |
Global Equivalents & Cross-Reference
Verwandt Materials
🧮 Material Weight Calculator
Calculate the weight based on this material's density: 8000 kg/m³
Frequently Asked Questions
Warum so expensive?
18% Ni + 9% Co + 5% Mo = >/kg raw material. Double vacuum melting (VIM+VAR). But der strength-toughness combination ist unmatched.
References & International Standards
- ASTM International. Norm Specifications für Stahl & Metal Alloys. astm.org
- International Organization für Standardization (ISO). Metallic Materials — Cross-Referenz Database. iso.org
- American Iron und Stahl Institute (AISI). Stahl Güte Designations & Equivalents. steel.org
- European Committee für Standardization (CEN). EN Stahl Standards & Numbering System. cencenelec.eu