EN 30CrNiMo8: Hoch-Hardenability Quenched & Tempered Stahl
EN 10083-3 · Published: 2026-06-02 · Updated: July 2026
EN 30CrNiMo8 (1.6580) is a medium-carbon nickel-chromium-molybdenum steel with 0.26-0.34% C, 1.80-2.20% Ni, 1.80-2.20% Cr, and 0.30-0.50% Mo—providing through-hardening capability in sections up to 200 mm. This deep hardenability combined with...
EN 30CrNiMo8 (1.6580) ist ein medium-carbon nickel-chromium-molybdenum steel mit 0.26-0.34% C, 1.80-2.20% Ni, 1.80-2.20% Cr, und 0.30-0.50% Mo—providing durch-hardening capability in sections auf zu 200 mm. Dies deep hardenability combined mit excellent niedrig-temperature toughness makes es der preferred material für large forged shafts, generator rotors, marine propeller shafts, und heavy-duty gear blanks in European heavy machinery. Der higher nickel content compared zu 34CrNiMo6 (4340) gives 30CrNiMo8 der edge für sehr large sections wo der core müssen achieve uniform properties. Available in forged bars auf zu 800 mm diameter von specialized mills.
Quick Facts
| Kategorie | Legierungsstahl |
| Norm | EN 10083-3 |
| Density | 7.85 g/cm³ |
| Yield Strength | 850 MPa (123 ksi) Q&T |
| Tensile Strength | 1,000 MPa (145 ksi) Q&T |
Global Equivalents & Cross-Reference
| Alternative Norm / Güte | Action |
|---|---|
| DIN 1.6580 | Compare |
| AISI 4340 (similar) | Compare |
| SNCM431 | Compare |
| 30CrNiMo8 | Compare |
Verwandt Materials
🧮 Material Weight Calculator
Calculate the weight based on this material's density: 7.85 g/cm³
Frequently Asked Questions
Können 30CrNiMo8 sein nitrided?
Ja, 30CrNiMo8 responds well zu gas nitriding bei 500-530°C für 30-60 hours, producing ein 0.3-0.6 mm deep hardened case mit 900-1,100 HV surface hardness. Der chromium content ensures gut nitride case formation. Nitriding ist applied zu large shafts und gears wo der core ist Q&T zu 850-1,000 MPa und der nitrided surface provides wear widerstand ohne der distortion von carburizing. Für maximum fatigue strength improvement, liquid (salt bath) nitrocarburizing ist auch effective.
References & International Standards
- ASTM International. Norm Specifications für Stahl & Metal Alloys. astm.org
- International Organization für Standardization (ISO). Metallic Materials — Cross-Referenz Database. iso.org
- American Iron und Stahl Institute (AISI). Stahl Güte Designations & Equivalents. steel.org
- European Committee für Standardization (CEN). EN Stahl Standards & Numbering System. cencenelec.eu