5052-H32 Aluminum Alloy: Marine-Güte Corrosion Resistant Sheet Metal Leitfaden
ASTM B209 / AMS 4016 · Published: 2026-06-02 · Updated: July 2026
5052 is an aluminum-magnesium alloy (2.2-2.8% Mg, 0.15-0.35% Cr) optimized for corrosion resistance rather than strength — it is the highest-strength non-heat-treatable aluminum alloy with excellent marine atmospheric corrosion resistance. The...
5052 ist ein aluminum-magnesium alloy (2.2-2.8% Mg, 0.15-0.35% Cr) optimized für corrosion widerstand rather als strength — es ist der highest-strength non-heat-treatable aluminum alloy mit excellent marine atmospheric corrosion widerstand. Der magnesium in fest solution provides modest fest-solution strengthening (cannot sein precipitation hardened — 5052 ist non-heat-treatable); der chromium refines grain structure und improves stress corrosion cracking widerstand. H32 temper (strain hardened und stabilized — 1/4 hard) ist der standard für sheet metal forming applications, providing ein optimal balance zwischen formability und strength.
5052-H32 ist der standard material für marine kraftstoff tanks, boat hulls, chemical storage tanks, electronic chassis, appliance panels, highway signs, und architectural sheet metal in coastal environments. Sein salt spray corrosion widerstand (ASTM B117, 1,000+ hours ohne pitting) qualifies es für marine und coastal verwenden ohne protective coating. Schweißeignung: excellent mit beide GTAW (TIG) und GMAW (MIG) using 5356 filler rod. Heat-affected zone (HAZ) strength loss ist minimal because 5052 ist non-heat-treatable — dort sind nein precipitates zu dissolve während welding. Für applications requiring higher strength mit similar corrosion widerstand, 5083-H321 (4.0-4.9% Mg) provides approximately 30% higher yield strength while maintaining excellent marine corrosion widerstand.
Quick Facts
| Kategorie | Aluminum Alloy |
| Norm | ASTM B209 / AMS 4016 |
| Density | 2680 kg/m³ |
| Yield Strength | 195 MPa (H32 temper) |
| Tensile Strength | 230 MPa |
Global Equivalents & Cross-Reference
| Alternative Standard / Grade | Action |
|---|---|
| AA 5052-H32 | Compare |
| AlMg2.5 (EN AW-5052) | Compare |
| A95052 (UNS) | Compare |
Verwandt Materials
🧮 Material Weight Calculator
Calculate the weight based on this material's density: 2680 kg/m³
Frequently Asked Questions
Können 5052 sein anodized?
Ja, 5052 anodizes well mit ein clear zu licht gray finish. However, der magnesium content causes ein slightly darker anodized color als 6061 oder 1100. Für decorative anodizing wo color consistency ist kritisch, 6061-T6 oder 1100-O kann sein preferred. Für functional anodizing (hard anodizing für wear widerstand), 5052 ist acceptable.
References & International Standards
- ASTM International. Norm Specifications für Stahl & Metal Alloys. astm.org
- International Organization für Standardization (ISO). Metallic Materials — Cross-Referenz Database. iso.org
- American Iron und Stahl Institute (AISI). Stahl Güte Designations & Equivalents. steel.org
- European Committee für Standardization (CEN). EN Stahl Standards & Numbering System. cencenelec.eu