Werkzeugstahl Materials

4 materials cross-referenced. Showing seite 1 von 1.

AISI H13 Hot Work Werkzeugstahl: Die Casting, Extrusion & Forging Die Properties

ASTM A681 / NADCA #207 / DIN 1.2344

Yield: 1100-1600 MPa (160-232 ksi) depending on tempering temperature · Equivalents: EN X40CrMoV5-1, DIN 1.2344, JIS SKD61, GB 4Cr5MoSiV1, Böhler W302

AISI D2 Cold Work Tool Steel: High-Carbon High-Chromium — Stamping, Blanking & Shear Blades

ASTM A681 / DIN 1.2379 / JIS SKD11

Yield: Compressive yield ~2200 MPa at 60 HRC · Equivalents: EN X153CrMoV12, DIN 1.2379, JIS SKD11, GB Cr12MoV, Böhler K110

AISI M2 High Speed Steel: Tungsten-Molybdenum — Cutting Tools, Drills & End Mills

ASTM A600 / ISO HS6-5-2C / DIN 1.3343

Yield: Compressive yield ~3000 MPa at 64 HRC · Equivalents: EN HS6-5-2C, DIN 1.3343, JIS SKH51, GB W6Mo5Cr4V2, Böhler S600

Ti-6Al-4V (Grade 5) Titanium Alloy: Aerospace, Medical Implant & High-Performance Properties

ASTM B265 / ASTM B348 / AMS 4911 / AMS 4928 / ISO 5832-3

Yield: 880 MPa (128 ksi) minimum (annealed) · Equivalents: EN 3.7165, DIN TiAl6V4, JIS TAP6400, GB TC4, UNS R56400